Methodology for Application of Damage Mechanics Approach to Model High Temperature Fatigue Damage Evolution in a Turbine Disc Superalloy.

Abstract

Aeroengine gas turbine components operate under complex loading environments. Turbine disc is one such component which experiences stresses at high temperature and accumulates life critical cyclic damage in the material during usage. This accumulation of cyclic damage results into significant deterioration in material strength which in turn may initiate the failure in these rotating components. This necessitates the need to develop an advanced lifing approach for fatigue life assessment of turbine disc. As there are no available standards for damage mechanics application, an attempt has been made in the present study to develop a methodology for application of damage mechanics approach to model high temperature fatigue damage evolution in a turbine disc Superalloy. High temperature (650 °C) stress-controlled fatigue tests on turbine disc alloy have been performed to evaluate parameters for damage mechanics based models. Using this approach, damage evolution has been simulated at specimen level. A good correlation has been observed in the damage mechanics based model's predicted damage and experimentally determined values.
Subjects
FATIGUE cracks; HIGH temperatures; DETERIORATION of materials; HEAT resistant alloys; FATIGUE life; ACCLIMATIZATION

Description